SG car chassis paint
You are here: Home » SG car chassis paint
Product Detail
Share to:

SGA automotive chassis paint

First, composition:
The paint is based on polymer resin, synthetic resin, natural resin and epoxy-type nano-materials after high-temperature refining, adding the solvent,
Black paint made of desiccant, wetting agent, etc., 20kg in single component packaging.
Second, performance and use:
The paint not only has excellent resistance to salt spray, impact resistance, high and low temperature resistance, water resistance, but also resistance to acid, alkali, electrical
The kinship also has very good results. It is especially suitable for chassis tanks and other metal materials for all types of large trucks, buses and cars.
Coatings on plastic and non-metal surfaces all play a very good role in protection.
Third, technical standards and test methods:
Items Indicators Testing method
Film color and appearance Black, smooth GB/T1729
Viscosity (coating a 4 cups) S 45—100 GB/T1729
Covering power g/m2       ≤ 40 GA2—502—67
Fineness um         ≤ 30 GB/T1724
Drying time h Dry  ≤ 1 GB/T1728
Hard work  ≤ 24
Impact strength kg.cm 50 GB/T1732
Adhesion level       ≤ 2 GB/T9286
Flexibility  mm 1 GB/ T1731
Water resistance (24h) Remove the paint film after 2h HG2—510—67
Petrol resistance (90#) 72h No change in film HG2—510—67
Acid resistance (immersed in 40% H2S04 solution for 72 hours) No change in film HG2018—57
Fourth, packaging, storage and transportation:
l, packing a single component, stir evenly to use, 20kg equipment, viscosity can add special thin material 5-8%, for plastic components surface, can add thinner material l: 1 = 100% thinner.
2. Storage: In the closed original condition, one year from the date of production, stored in ventilated and dry place, and away from the fire.
V. Construction Notice:
Before the above SGA, SGB two kinds of paint construction coating, the steel surface and the non-metal surface are first processed clean, and the same treatment as normal paint, the steel surface to meet the secondary rust standards and can be painted. One-component, open the barrel after mixing with special thinner adjustment to about 40 seconds and can be painted; two-component, generally 4:1 after mixing with special thinner the same adjustment to 40 seconds and can be painted, thinner material 5-8%. Brush, spray, dip.