JL890 High build epoxy antirust paint

Introduction 2K high performance high build epoxy antirust paint comprising epoxy resin, aluminum powder 
antirust pigment, additives and solvent,etc.
Applications Applicable to the ship bottom , ballast tanks, hull, wharf, steel pile,offshore oil drilling platform, 
hydraulic steel gates, mine steel 
supports and pipelines,used as anticorrosion paint.
Properties Excellent water resistance and rust resistance, good cathodic protection    performance,good    
resistance to chemicals  and oil;
excellent crude oil resistance.
Film thickness
and     spreading
rate
DFT:125μm     Theoretical spreading rate: 280g/ m /125μm    WFT: 208μm
Physical
performance
Appearance:JL890-1    bronze            JL890-2    light gray
Volume solid:60±3%
Flash point: >27℃
Viscosity:
Surface
pretreatment
Sandblasting to Sa2.5 as described in ISO standard, and surface roughness between 40-70μm; or St2 for surface treatment is required if using power tool.
Application
parameters
Ratio: A:B = 100:28 (by weight)
Coating method
Airless spraying: recommended conditions: inlet pressure:
5kgf/ cm , compression ratio: 1:65,
Type of nozzle: flow / spraying width ––26/30    32/35
  Brushing : A precoating or small area of painting is recommended,but the dry film thickness must    
meet the specified requirements.

Roller coating: Can be used in a small area of painting,but the dry film thickness must   meet the specified requirements.
Thinner:    thinner JL103
Pot life :    25℃/2.5h
Recommended coating layer(s):used for bottom antirust, 4 layers, with its DFT 400μm used for 
land steel structure anticorrosive, 2 layers, with its DFT 
200μm
Drying process
Substrate
temperature
Touch dry Hard dry recoating interval
shortest longest
5℃ 5h 8h 9h 7d
20℃ 3.5h 6h 7h 4d
30℃ 2.5h 4h 5h 3d
Application
conditions
The substrate temperature≥ 5℃ and at least 3℃ higher than the dew point of the air temperature; 
The temperature and relative humidity 
shall be measured nearby the substrate to be coated;      
relative 
humidity ≤ 85%;Good ventilation is required useful for film drying process.
Typical coating
compatibility
Preceding coats: epoxy iron red, epoxy zinc rich, and inorganic zinc silicate shop primer.
Subsequent coats: epoxy, chlorinated rubber, polyurethane, acrylic and fluorocarbon topcoat.
Storage The product must be stored under standard conditions as described by related state regulations,
 wherein the environment must be dry, cool,
well ventilated and away from heat and/or fire. 
The packaging  
containers must be kept sealed.
Load and
unload
Cautious operation; Stir well before use.
Packaging
specifications
A:    20L/12kg
B:    4L/3.3kg
Health           and
safety
Please note the warning logo labeled on packaging container and operate in a circumstance with 
good ventilation, avoid swallowing or inhaling 
paint mist, avoid skin contact or use suitable 
detergent, soap and 
water to clean immediately if the paint splashed on the skin, and use
flowing clean water to rinse eyes if splashed, or carry on medical care immediately. For more details 
about health and safety as well as the 
cautions of the product, please refer to our "product safety 
manual"
MSDS.
Claim The information given on this product manual is derived from experiments and practical applications. 
We only guarantee the quality
,of the said product since conditions of use are beyond the manufactures
control. We reserve the rights to revise the specifications of the product without prior notice.