JL846 High build epoxy asphalt antirust paint

Introduction 2K high performance antirust paint comprising epoxy resin, coal tar pitch, 
epoxy curing agent, aluminum powder, iron oxide antirust 
pigment, inert 
pigment, additives and solvent,etc.
Applications Applicable to the ship bottom, water ballast tank, steel pier piles, offshore 
oil drilling platform, hydraulic steel gates, mine steel 
supports,insideand    
outside the wall of  pipeline, used as 
anticorrosion paint.
Properties Excellent water resistance and rust resistance, excellent resistance 
tochemicalsand  oil;  good adhesion,impact resistance           and wearability. Good cathodic protection performance. The dry film 
thickness(DFT) can reach 125 μ m each time when airless spraying,
saving the cost.
Film thickness
and     spreading
rate
DFT:125μm    Theoretical spreading rate:JL846-1    220g/ m2
WFT: 187μm                                                       JL846-2    224g/ m2
Physical
performance
Appearance:JL846-1    silver brown            JL846-2    black
Volume solid:67±3%
Flash point: 22℃
Viscosity:    3~5 pa·s
Surface
pretreatment
Sandblasting to Sa2.5 as described in ISO standard, and surface roughness 
between 40-70μm; or St2 for surface treatment is required 
if using power tool.
Application
parameters
Ratio: A:B = 7:4 (by weight)
Coating method
Airless spraying: recommended conditions: inlet pressure:
5kgf/ cm , compression ratio: 1:65,
Type of nozzle: flow / spraying width ––26/30    32/35
Brushing : A precoating or small area of painting is recommended,but the dry film 
thickness must  meet the specified requirements.

Roller coating:  Can be used in a small area of painting,but the dry film thickness 
must  meet the specified requirements.

Thinner:    thinner JL103
Pot life :    25℃/6h
Recommended coating layer(s):  JL846-1、JL846-2 each 1 layer, with its
DFT ≥250μm
Drying process
Substrate
temperature
Touch dry Hard dry recoating interval
shortest longest
5℃ 8h 48h 48h 14d
20℃ 4h 24h 24h 7d
30℃ 2h 16h 16h 5d
Application
conditions
The substrate temperature≥ 5℃ and at least 3℃ higher than the dew point of the 
air temperature; The temperature and relative humidity 
shall be measured nearby 
the substrate to be coated;relative 
humidity ≤ 85%;Good ventilation is required 
useful for film drying 
process.
Typical coating
compatibility
Preceding coats: all shop primer, JL842 Epoxy Mio antirust paint or coating on the 
steel plate directly.
Subsequent coats: when as bottom primer, coating JL616 
chlorinated 
rubber intercoat then antifouling paint.
Storage The product must be stored under standard conditions as described by related state 
regulations, wherein the environment must be dry, cool,
well ventilated and away from
 heat and/or fire. The packaging
  containers must be kept sealed.
Load and
unload
Cautious operation; Stir well before use.
Packaging
specifications
A:    20L/14kg
B:    10L/8kg
Health           and
safety
Please note the warning logo labeled on packaging container and operate in a circumstance 
with good ventilation, avoid swallowing or inhaling 
paint mist, avoid skin contact or use suitable 
detergent, soap and 
water to clean immediately if the paint splashed on the skin, and use 
flowing clean water to rinse eyes if splashed, or carry on medical care immediately. For more 
details about health and safety as well as the 
cautions of the product, please refer to our "product 
safety manual"
MSDS.
Claim The information given on this product manual is derived from experiments and practical applications. 
We only guarantee the quality
,of the said product since conditions of use are beyond the manufactures
control. We reserve the rights to revise the specifications of the product without prior notice.