JL616 High build chlorinated rubber iron oxide antirust paint (intercoat)

Introduction A antirust paint comprising chlorinated rubber, iron oxide antirust pigments, plasticizer, 
additives and solvents,etc.
Applications Applicable to the ship bottom antirust and ship waterline, sea steel structurebuildings    
and other steel strucures for corrosion protecton.Also can be used as intercoat in ship
bottom 
antifoulingpaint.
Properties Poor permeability of gas to the paint film, excellent water resistance,good corrosion 
resistance and decoration performance. Fast drying, dry 
faster than oily paint several 
times, excellent low temperature 
construction performance down to -20 ℃ ~50 ℃ . 
Excellent alkali 
resistance and durability. good adhesion to steel. Good performance
of recoating on the old paint film, convenient repairment.
Film thickness
and     spreading
rate
DFT:75μm       Theoretical spreading rate:236g/ m /75μm     WFT: 179μm
Physical
performance
Appearance:iron red
Volume solid:42±3%
Flash point: 31℃
Viscosity:
Surface
pretreatment
Sandblasting to Sa2.5 as described in ISO standard, and surface roughness between 40-70μm; or St2 for surface treatment is required  if using power tool.
Application
parameters
Proportion: one component
Coating method
  Airless spraying: recommended conditions: inlet pressure:
4~5kgf/ cm , compression ratio: 1:65,
Type of nozzle: flow / spraying width ––19/30    26/35
Brushing : A precoating or small area of painting is recommended,
but the dry film thickness must  meet the specified requirements.
Roller coating: Can be used in a small area of painting,but the
dry film thickness must    meet the specified requirements.
Thinner:  thinner JL101
Pot life :  No limit
Recommended coating layer(s):    2 layers, with its DFT 150μm
Drying process
Substrate
temperature
Touch dry Hard dry recoating interval
shortest longest
5℃ 4h 24h 12h No limit
20℃ 2h 12h 8h No limit
30℃ 1h 8h 6h No limit
Application
conditions
The substrate temperature≥ 5℃ and at least 3℃ higher than the dew point of the air 
temperature; The temperature and relative humidity 
shall be measured nearby the 
substrate to be coated; relative 
humidity ≤ 85%;Good ventilation is required useful for   film drying  process.
Typical coating
compatibility
Preceding coats: JL615,JL846,JL546,etc.
Subsequent    coats:    various    colour    chlorinated    rubber    topcoat,
JL839,JL837 antifouling paint.
Storage The product must be stored under standard conditions as described by
related state regulations, wherein the environment must be dry, cool,
well ventilated and away from heat and/or fire. The packaging
containers must be kept sealed.
Load and
unload
Cautious operation; Stir well before use.
Packaging
specifications
20L/26kg
Health           and
safety
Please note the warning logo labeled on packaging container and operate in a 
circumstance with good ventilation, avoid swallowing or inhaling 
paint mist, avoid 
skin contact or use suitable detergent, soap and 
water to clean immediately if the
 paint splashed on the skin, and use 
flowing clean water to rinse eyes if splashed,
 or carry on medical care 
immediately. For more details about health and safety 
as well as the 
cautions of the product, please refer to our "product safety manual"
MSDS.
Claim The information given on this product manual is derived from experiments and 
practical applications. We only guarantee the quality
,of the said product since 
conditions of use are beyond the manufactures 
control. We reserve the rights 
to revise the specifications of the 
product without prior notice.