JL615 Chlorinated rubber aluminum antirust paint

Introduction A antirust paint comprising chlorinated rubber, plasticizer, aluminum powder antirust pigments, 
additives and solvents,etc.
Applications Applicable to the ship bottom and waterline, hull, superstructure, sea and land steel structure 
building for corrosion protection.
Properties Poor permeability of water vapor and oxygen to the paint film, excellent water resistance, good 
corrosion resistance and decoration 
performance. Fast drying, dry faster than oily paint several 
times, 
excellent low temperature construction performance down to -20℃~50℃ . good adhesion 
to steel, excellent alkali resistance and 
durability.Excellent mutual solubility and good adhesion 
between the 
film layers, recoating on the old paint film, without removal of the solid old film, 
convenient repairment. Unsaponifiable in seawater,
good compatibility with cathodic protection.
Film thickness
and     spreading
rate
DFT:60μm       Theoretical spreading rate:193g/ m /60μm    WFT: 143μm
Physical
performance
Appearance:Silver gray
Volume solid:42±3%
Flash point: 31℃
Viscosity:
Surface
pretreatment
Sandblasting to Sa2.5 as described in ISO standard, and surface roughness between 40to70μm; 
or St2 for surface treatment is required 
if using power tool.
Application
parameters
Proportion: one component
Coating method
Airless spraying: recommended conditions: inlet pressure:
3~4kgf/ cm , compression ratio: 1:65,
Type of nozzle: flow / spraying width ––19/30    26/35
Brushing : A precoating or small area of painting is recommended,
but the dry film thickness must    meet the specified requirements.
Roller coating:    suitable for use, but the dry film thickness must
meet the specified requirements.
Thinner:  thinner JL101
Pot life :  No limit
  Recommended coating layer(s):    2 layers, with its DFT 120μm
Drying process
Substrate
temperature
Touch dry Hard dry recoating interval
shortest longest
5℃ ≤4h 24h 12h No limit
20℃ ≤2h 12h 8h No limit
30℃ ≤1h 8h 6h No limit
Application
conditions
The substrate temperature≥ 5℃ and at least 3℃ higher than the dew point of the air temperature; 
The temperature and relative humidity 
shall be measured nearby the substrate to be coated;relative 
humidity ≤ 85%;Good ventilation is required useful for film drying process.
Typical coating
compatibility
Preceding coats: epoxy shop primer, inorganic zinc silicate shop primer Subsequent coats: 
JL616 high build chlorinated rubber iron oxide
antirust paint, or chlorinated rubber topcoat
Storage The product must be stored under standard conditions as described by related state regulations, 
wherein the environmentmust be dry, cool,
well ventilated and away from heat and/or fire. 
The packaging 
containers must be kept sealed.
Load and
unload
Cautious operation; Stir well before use.
Packaging
specifications
20L/24kg
Health      and
safety
Please note the warning logo labeled on packaging container and operate in a circumstance 
with good ventilation, avoid swallowing or inhaling 
paint mist, avoid skin contact or use suitable 
detergent, soap and 
water to clean immediately if the paint splashed on the skin, and use flowing 
clean water to rinse eyes if splashed, or carry on medical care 
immediately. For more details 
about health and safety as well as the 
cautions of the product, please refer to our "product 
safety manual"
MSDS.
Claim The information given on this product manual is derived from experiments and practical applications. 
We only guarantee the quality
,of the said product since conditions of use are beyond the manufacture
control. We reserve the rights to revise the specifications of the product without prior 
notice.