| Introduction | 2K epoxy intercoat. |
| Applications | Used as intercoat between ship bottom antirust paint and antifouling paint, also can be used as intercoat between antirust primer and decorative topcoat, protecting the primer coating, enhance the whole coating internal adhesion and protection performance. |
| Properties | Good layer-to-layer adhesion both to the preceding and subsequent coating. Excellent antirust performance and durability, good compatibility with coating system based on epoxy, polyurethane and acrylic. |
| Film thickness and spreading rate |
DFT：100μm Theoretical spreading rate：256g/ m /100μm WFT: 180μm |
| Physical performance |
Appearance：matt and gray Volume solid：56±3% Flash point：part A: 38℃ part B: 20℃ Viscosity: |
| Surface pretreatment |
Sandblasting to Sa2.5 as described in ISO standard, and surface roughness between 40-70μm; or St2 for surface treatment is required if using power tool. |
| Application parameters |
Ratio: A:B=100:14.8 (by weight) Coating method Airless spraying: recommended conditions: inlet pressure: 4~5kgf/ cm , compression ratio: 1:65, Type of nozzle: flow / spraying width ––19/30 26/35 |
| Brushing : A precoating or small area of painting is recommended, but the dry film thickness must meet the specified requirements. Roller coating: Can be used in a small area of painting,but the dry film thickness must meet the specified requirements. Thinner: thinner JL103 Pot life : 25℃/6h Recommended coating layer(s): 1 layer, with its DFT 100μm Drying process |
|||||
| Substrate temperature |
Touch dry | Hard dry | recoating interval | ||
| shortest | longest | ||||
| 5℃ | 12h | 24h | 24h | 5d | |
| 20℃ | 8h | 19h | 12h | 5d | |
| 30℃ | 5h | 14h | 6h | 5d | |
| Application conditions |
The substrate temperature≥ 5℃ and at least 3℃ higher than the dew point of the air temperature; The temperature and relative humidity shall be measured nearby the substrate to be coated;relative humidity ≤ 85%;Good ventilation is required useful for film drying process. |
||||
| Typical coating compatibility |
Preceding coats: coating on the recommended epoxy antirust paint. Subsequent coats: ship bottom antifouling paint,epoxy, polyurethane,chlorinated rubber and acrylic topcoat. |
||||
| Storage | The product must be stored under standard conditions as described by related state regulations, wherein the environment must be dry, cool,well ventilated and away from heat and/or fire. The packaging containers must be kept sealed. |
||||
| Load and unload |
Cautious operation; Stir well before use. | ||||
| Packaging specifications |
A: 20L/25kg B: 4L/3.7kg |
||||
| Health and | Please note the warning logo labeled on packaging container and operate | ||||
| safety | in a circumstance with good ventilation, avoid swallowing or inhaling paint mist, avoid skin contact or use suitable detergent, soap and water to clean immediately if the paint splashed on the skin, and use flowing clean water to rinse eyes if splashed, or carry on medical care immediately. For more details about health and safety as well as the cautions of the product, please refer to our "product safety manual"MSDS. |
| Claim | The information given on this product manual is derived from experiments and practical applications. We only guarantee the quality,of the said product since conditions of use are beyond the manufactures control. We reserve the rights to revise the specifications of the product without prior notice. |