High-temperature coating clay, putty

Frist, Composition: Silicone resin, polyester epoxy resin, hollow microspheres, special temperature-resistant anti-corrosive pigments, fillers, additives, curing agents, organic solvents, etc., and the bottom surface is A or B packaging or A, B, C three packs.
Second color: primer, iron red, gray
Third, performance: heat, sudden change in temperature, can be long-term temperature below 200-400 °C and 400 °C, room temperature from the dry curing, the bottom of the supporting force, corrosion resistance, chemical atmosphere, acid, water, humidity, weathering , has a good corrosive.
Fourth, use: used for blast furnace hot blast furnace inner and outer wall, chimney, flue, drying tunnel, exhaust pipe, high heat gas pipeline, heating furnace, heat exchanger and other non-metal and metal surface high temperature corrosion protection, can be used for metal and non- Metal temperature resistant plaster, putty use, brushing, scraping, can be solidly bonded to the surface layer.
Fifth,Performance indicators
No items   index
1 Slurry PH   7-8
2 Slurry density Kg/m3 <1000
3 Dry density Kg/m3 <250
4 Slurry shrinkage % <2.5
5 tensile strength MPa After 600 °C -800 °C constant temperature 1h> 0.1
6 Bond strength KPa 600 °C -800 °C constant temperature 1h> 25
7 Resistance to cold and hot
-40°C-105°C Alternating
  Coating does not crack or fall off
8 Impact resistance   250g steel ball 1.5m high impact three times, the coating does not fall off
9 Thermal conductivity average temperature 400°C w/m.l <0.05
10 Acid resistance   Soaked in 20% H2SO4 solution for 24 hours without cracking, falling off, insoluble
Six, surface treatment
(1) The surface of the metal steel must be shot blasted or sandblasted or polished to a St2 grade.
(2) The surface of maintenance work can be manually derusted to reach St2 level.
Seven, it is recommended that the number of coating channels: according to the need for coating thickness.
VIII, storage period: 6 months.
Nine, packaging specifications: Group A 20kg, Group B 5kg, 4 to 1 to use. The clay is set according to the application. 1 to 1, 1 to 1.5, and 1 to 2 can be used.
X. Security Measures:
(1) The paint should be placed in a ventilated and dry place away from the fire to avoid direct sunlight.
(2) No open fire at the construction site
(3) In the construction of enclosed places, ventilation must be emphasized. Painters and constructors should wear protective equipment to avoid poisoning.
(4) The electric welding can not be painted immediately after completion, because of the high temperature and high solvent volatilization, affecting the coating quality and construction safety.
(5) Before the paint film is completely dry or the film is cured, protective measures shall be taken to prevent it from being washed and trampled by rain and other liquids.