H06-7 metal tank conductive primer

project Explain
composition
 
performance
 
use
 
 
Coating method
Thinner
Construction viscosity
Coating thickness
Usage amount
Matching ratio
Aging period
Applicable period
Painting interval
Relative humidity
After the matching paint
 
 
 
Storage period
The coating is mainly composed of alkyl silicate, ultra-fine zinc powder, pigment filler, special auxiliaries, curing agent and the like. Two-component packaging.
Has excellent electrical conductivity and heat resistance, sudden temperature change, and has the advantages of fast drying, strong adhesion, easy construction and so on.
Suitable for metal tank static primer and blast furnace hot blast stove outer wall and chimney, flue, drying tunnel, exhaust pipe, high temperature hot gas pipeline heating furnace, and other metals require high temperature anti-corrosion equipment special primer and shop primer .
Brush, roller, spray.
H06-7 special thinner
Brush for 25-30 seconds Spray 15-20 μm/channel
Brush 20-25um/channel, spray 15-20 microns/channel
Brushing 140 to 170 g/m2, spraying 150 to 180 g/m2
Group A: Group B = 4:l
20 minutes
8 hours
The shortest 5 hours The longest 24 hours
Less than 85%
H06-7 anti-static anti-static special anti-corrosion coating for metal oil tanks, H06-3 epoxy anti-corrosion paint cloud iron, a variety of epoxy topcoats, WEH88 series silicone high temperature finish.
12 months
Technical indicators:
project index Detection method
Exterior gray Visual inspection
Viscosity (coating a 4 cups) S ≥ 25 GBl723—79
Adhesion level ≤ 2 GBl720一79
Flexibility mm ≤ 3 GBl73l一79
Drying time H (23±2℃) Dry ≤ 0.5 GBl728一79
Hard work ≤ 12
Technical indicators:
project index Detection method
Exterior gray Visual inspection
Viscosity (coating a 4 cups) S ≥ 25 GBl723—79
Adhesion level ≤ 2 GBl720一79
Flexibility mm ≤ 3 GBl73l一79
Drying time H (23±2℃) Dry ≤ 0.5 GBl728一79
Hard work ≤ 12